Stress and creep damage evolution in materials for USC power plants.
В наличии
Местонахождение: Алматы | Состояние экземпляра: новый |
Бумажная
версия
версия
Автор: Sanjooram Paddea
ISBN: 9783659527753
Год издания: 2014
Формат книги: 60×90/16 (145×215 мм)
Количество страниц: 344
Издательство: LAP LAMBERT Academic Publishing
Цена: 56528 тг
Положить в корзину
Способы доставки в город Алматы * комплектация (срок до отгрузки) не более 2 рабочих дней |
Самовывоз из города Алматы (пункты самовывоза партнёра CDEK) |
Курьерская доставка CDEK из города Москва |
Доставка Почтой России из города Москва |
Аннотация: The so-called creep strength enhanced ferritic 9-12% Cr steels have been identified as the most promising class of materials for some of the key components in ultra-supercritical fossil-fired power plants, including the main steam pipes, headers and superheater tubings. These steels are less costly, and they have a lower coefficient of thermal expansion and a higher thermal conductivity when compared with austenitic stainless steels, making them less susceptible to degradation through thermal fatigue. However, experience has shown that the weldments in these steels are particularly prone to premature creep failure, due to a localised form of cracking in the heat-affected zone, which is referred to as Type IV cracking. The work presented in this thesis is concerned with the effects of residual stresses and constraint on Type IV cracking. It was found that the highest as-welded tensile stresses resided near the outer boundary of the HAZ, and towards the weld root region and these were not fully relieved by the applied PWHT. In both conditions substantial tensile direct and hydrostatic stresses existed across the HAZ, including the fine-grained and intercritically-annealed regions.
Ключевые слова: Phase transformation, creep, residual stress, Phase transformation, creep, ferritic steel, P91, Type IV cracking