Al6061-GRAPHITE-TUNGSTEN CARBIDE HYBRID COMPOSITES. SYNTHESIS AND PROPERTY EVALUATION
В наличии
Местонахождение: Алматы | Состояние экземпляра: новый |
Бумажная
версия
версия
Автор: A. Ramesh,A.R. KARIBASAVA SWAMY and DEEPAK. S
ISBN: 9786202799584
Год издания: 2020
Формат книги: 60×90/16 (145×215 мм)
Количество страниц: 204
Издательство: LAP LAMBERT Academic Publishing
Цена: 43812 тг
Положить в корзину
Способы доставки в город Алматы * комплектация (срок до отгрузки) не более 2 рабочих дней |
Самовывоз из города Алматы (пункты самовывоза партнёра CDEK) |
Курьерская доставка CDEK из города Москва |
Доставка Почтой России из города Москва |
Аннотация: This Book describes the investigations carried out on base Al6061 alloy, Al6061-WC MMCs and Al6061-WC-Gr MMHCs. The composites were developed by liquid metallurgy technique. In the development of Al6061-WC MMCs and Al6061-WC-Gr MMHCs the tungsten carbide of 1-4 wt% used as a primary reinforcement, and a constant 4 wt% graphite (Gr) used as a secondary reinforcements in Al6061-WC-Gr MMHCs.The manufactured composites were treated with T6 heat treatment for different ageing times of 1, 3 and 5 h. As-cast and heat treated composites were characterized for their physical, mechanical and tribological properties. The mechanical and wear properties were investigated according to the ASTM standard testing procedures. The composites properties were investigated in as- cast and heat treated conditions.Scanning Electron Micrographs (SEM) of tensile fracture surfaces of the MMCs and MMHCs revealed that there was an excellent bond between matrix and reinforcements. The strong bond allows the effective transfer of applied load between the matrix and reinforcements. The fractured surfaces confirm the brittle failure mechanism of the composites.
Ключевые слова: matrix, Primary reinforcement, Secondary reinforcement, Metal matrix composites, Metal Matrix Hybrid Composites, heat treatment, Hardness, Ultimate Tensile Strength, ductility, wear rate